箱体铸件,case casting
1)case casting箱体铸件
1.Based on the configuration characteristics of the large nodular iron case casting,the casting method,gating system and relevant process parameters was selected.解决了大型箱体铸件内孔同轴度不一致的问题,并通过采用CAE模拟软件分析铸件的缺陷,完善其铸造工艺、降低产品的开发风险。
1.Application of EPC Casting Used for Large-size Box-body Casting消失模铸造在大型箱体铸件生产中的应用
2.Transfer case,different size Hydrant;Compreser body precisicen casting; Duefile casting; Wear high-chromium iron casting and heating-proof casting.变速箱、消防栓壳体系列；制冷压缩机精密铸件；球铁铸件；耐磨高铬铸铁件及耐热件。
3.Practice and Research of Box Section Shape and Thin Wall Steel Castings with Furan Resin Sand;呋喃树脂砂生产薄壁箱体铸钢件的实践与研究
4.Casting Technique of Large-Scale Aluminum Gearbox Block Used for High-Speed Train高速列车用大型铸铝齿轮箱箱体铸造工艺
5.crossbar of the mo(u)lding box(铸造)箱筋, 箱挡
6.The Experimentation Study of the Low-pressure Foundry Techniques of the Hull Castings;壳体类铸件的低压铸造工艺试验研究
7.Cast Technology of Cast-steel Shell Based on ProCAST基于ProCAST的铸钢件壳体铸造工艺研究
8.Application of low pressure casting in Al-Si shell casting parts低压铸造在铝硅壳体类铸件中的应用
9.Improvement on Casting Process for Frame Casting of Magnesium Alloys某型框架体镁合金铸件铸造工艺改进
10.Technical Improvement for ZG15Cr1Mo1V Valve Body CastingsZG15Cr1Mo1V阀体铸件工艺的改进
11.Development of GGG40.3 Grade Nodular Iron Valve Body CastingGGG40.3球铁阀体铸件的研制
12.Quality-control and Production of the Die Casting Cylinder-Block and Transmission Case发动机缸体与变速箱壳体压铸生产及质量控制
13.Application of CAE Technology on Casting Process Optimization of Expander Bearing BoxCAE技术在轴承箱体铸造工艺优化中的应用
14.Structure made of pearlitic stabilized cast-iron with parts in stabilized steel.珠光体铸铁机架，部分部件高强度钢铸造。
15.Study on Dimensional Accuracy of High Strength Gray Iron Cylinder Block Castings with Thin Section Thickness高强度薄壁灰铸铁缸体铸件尺寸精度研究
16.Analysis on the Cast Condition Graphite in Production of the Ferrite Nodular Graphite Malleable Casts铁素体球墨可锻铸铁件生产中铸态石墨的分析
17.Using the FEM, the deformation and stress field of a large-scale Mg alloy die casting machine have been calculated by ANSYS.压铸机的整体变形情况对压铸机性能和铸件质量有重要影响。
18.The castings made by founding.铸件铸造出来的物件
Cast iron case casting箱体铸铁件
3)calculation of dimension of box bodx casting箱体铸件尺寸计算
4)cast housing铸造箱体
5)saggar[英]['s?g?][美]['s?g?]铸件退火箱
6)cylinder casting缸体铸件
中国古代韧性铸铁件 韧性铸铁亦称可锻铸铁，是古代生铁铸件中的重要品种之一。它是用白口铁在较高温度下经过长时间退火(900℃， 3～5天)，使脆硬的碳化铁分解，析出絮状石墨，从而使硬而脆的生铁变为韧性较好的制品。如果铸件表面脱碳而中心部分仍为白口铁，则为韧化处理不完全的韧性铸铁。迄今所知世界最早的韧性铸铁件是洛阳出土的公元前 6世纪战国铁铲。 战国中期以后，韧性铸铁已在燕、赵、魏、楚等国的广大地域内广泛应用，如湖北省大冶铜绿山出土的战国晚期铁斧和河北省易县燕下都 44 号墓出土的战国晚期铁??、六角锄、都具有韧性铸铁的组织。在河南省巩县铁生沟"河三"、郑州古荥"河一"遗址以及渑池、南阳等汉代冶铸遗址出土的大批铁器中，也都发现了韧性铸铁农具和工具。 汉代对韧性铸铁能更合理地选用，如南阳瓦房庄遗址所出的铁农具,经检验的12件中有 9件是韧性铸铁,而手工工具、兵器等则没有发现韧性铸铁；铁生沟出土的铁器，经鉴定为韧性铸铁的农具、工具占检验铁器总数的20.5％,满城汉墓出土的铁铲(2:003)、铁镢(1:4397)等都是采用了可锻化热处理得到的白心韧性铸铁器。汉代的韧性铸铁件质量相当稳定，其退火石墨多呈典型的团絮状，且分布均匀。一般对需要较好耐冲击性和较高强度的斧、凿、锛等手工工具，需选用基体含碳较高的韧性铸铁，而对要求较高韧性和较好耐磨性的铲、锄等农具则选用基体含碳不多的韧性铸铁。渑池汉魏窖藏的犁铧(166号)等器物也是韧性铸铁件,说明此时韧性铸铁得到更广泛的应用。直到唐代仍偶尔使用韧性铸铁农具，但以后再无发现。欧洲韧性铸铁的发现最早见于1722年出版的著作中，中国韧性铸铁的发明及使用比欧洲早了2200多年。