摘要: 通过对覆膜全过程的分析和优化实验, 确定影响覆膜砂性能的工艺因素主要有: 原砂的加热温度、
加入树脂后的混砂时间、加入固化剂的混砂时间等, 为了获得最佳的工艺参数, 对各个工艺参数进行了正交实
验。实验结果表明: 为获得较高的热态抗拉强度, 可以选用砂温180℃, 加树脂后的混砂时间为100s , 加固化
剂后的混制时间为40s , 加硬脂酸钙后的混制时间为30s ; 为获得较好的常温抗拉强度, 可以选用砂温
180℃, 加树脂后的混砂时间为80s , 加固化剂后的混制时间为30s , 加硬脂酸钙后的混制时间为20s 。
关键词: 覆膜砂, 工艺参数, 实验研究
中图分类号: TG221+. 2-文献标识码: A; 文章编号: 1006- 9658 ( 2007 ) 06- 4
Abs tract: By analyzing and optimizing the proces s of shell molding,the main factors affecting the
properties of res in coated sand have been obtained,such as the heating temperature of original sands ,
the mixing time after adding res in and the mixing time after adding solidified agent, etc.In order to achieve
better proces s ing parameters ,orthogonal experiments have been carried out.The results showed that,
when the temperature of sands was 180℃, the mixing time was 100s , the mixing time after adding solidified
agent was 40s and the mixing time after adding calcium s tearate was 30s ,higher tens ile s trength in
hot condition could be got.At the same time,to obtain higher tens ile s trength in normal temperature,the
temperature of sands was 180℃ ,the mixing time was 80s ,the mixing time after adding solidified agent
was 30s and the mixing time after adding calcium s tearate was 20s .
Keywords : Res in coated sand , Technological parameter, Experimental research
收稿日期: 2007- 06- 12
文章编号: 2007- 092
作者简介: 梁春永( 1976- ) , 男, 河北唐山人, 讲师, 在读博士。主要从
事造型材料、生物医学材料、材料检测等方面的研究工作
!!!!!!!!!!!!!!!!!!!!!!!!!!!!!!!!!!!!!!!!!!!!!!
28
CFMT 中国铸造装备与技术6 / 2007
应用于复杂铸件的生产, 如汽车、拖拉机的发动机缸
体、缸盖、进气管及排气管等[1]。在我国, 随着铸造技
术的发展, 对铸件质量的要求也越来越高, 为此覆膜
砂的用量将会越来越多。酚醛树脂壳法工艺之所以
倍受广大铸造工作者的青睐, 主要原因是该法工艺
稳定, 技术成熟, 生产成本不高, 操作简便, 型( 芯) 致
密紧实, 砂型( 芯) 及型( 芯) 砂的存放性好, 易于大批
量生产, 可生产表面光洁、尺寸精度较高的近无余量
的中小钢、铁及铝合金铸件[2]。因此长期以来, 该工艺
一直是大批量铸造生产过程中的必要的组成部分。
但是国产覆膜砂在总体性能上与国际水平相差较
大。混砂过程和覆膜条件是影响覆膜砂质量的关键
因素, 为了提高覆膜砂的质量, 本文从覆膜砂生产工
艺入手, 对影响覆膜砂性能的几个重要因素进行了
分析, 以期得到更佳性能的覆膜砂的生产工艺。
1 实验方法
1.1 实验用材料
原砂: 内蒙古大林普通原砂, 粒度为70～140 目;
树脂: 酚醛树脂( 国内某厂生产的商品树脂) ; 其它材
料: 乌洛托品的加入量为14%( 占树脂量) 和硬脂酸
钙。
1